Stability of three-phase ternary-eutectic growth patterns in thin sample

Abstract : Near-eutectic ternary alloys subjected to thin-sample directional solidification can exhibit stationary periodic growth patterns with an ABAC repeat unit, where A, B and C are the three solid phases in equilibrium with the liquid at the eutectic point. We present an in-situ experimental study of the dynamical features of such patterns in a near-eutectic In-In 2 Bi-Sn alloy. We demonstrate that ABAC patterns have a wide stability range of spacing at given growth rate. We study quantitatively the-di↵usion process that is responsible for the spacing uniformity of steady-state patterns inside the stability interval. The instability processes that determine the limits of this interval are examined. Qualitatively, we show that ternary-eutectic ABAC patterns essentially have the same dynamical features as two-phase binary-eutectic patterns. However, lamella elimination (low-stability limit) occurs before any Eckhaus instability manifests itself. We also report observations of stationary patterns with an [AB] m [AC] n superstructure, where m and n are integers larger than unity.
Document type :
Journal articles
Complete list of metadata

Cited literature [18 references]  Display  Hide  Download

https://hal.archives-ouvertes.fr/hal-01472485
Contributor : Silvère Akamatsu Connect in order to contact the contributor
Submitted on : Monday, February 20, 2017 - 5:54:36 PM
Last modification on : Saturday, January 15, 2022 - 3:44:16 AM
Long-term archiving on: : Sunday, May 21, 2017 - 3:48:21 PM

File

InBiSn_1.pdf
Files produced by the author(s)

Identifiers

Citation

S Bottin-Rousseau, M S ̧erefog ̆lu, Sinan Yücetürk, Gabriel Faivre, Silvère Akamatsu. Stability of three-phase ternary-eutectic growth patterns in thin sample. Acta Materialia, Elsevier, 2016, 109, pp.259 - 266. ⟨10.1016/j.actamat.2016.01.065⟩. ⟨hal-01472485⟩

Share

Metrics

Record views

77

Files downloads

153