ZSM-5/SBA-15 microporous/mesoporous composites prepared by a microwave-assisted zeolitisation of Al-SBA-15 mesoporous solids - Archive ouverte HAL Access content directly
Journal Articles Materials Research Bulletin Year : 2013

ZSM-5/SBA-15 microporous/mesoporous composites prepared by a microwave-assisted zeolitisation of Al-SBA-15 mesoporous solids

(1) , (2) , (1) , (3) , (4) , (2) , (2) , (3) , (5) , (4)
1
2
3
4
5

Abstract

ZSM-5/SBA-15 composites with high textural properties were synthesised by a microwave-assisted zeolitisation of Al-SBA-15 in the presence of tetrapropylammonium bromide. The effect of the hydrothermal treatment temperature and of ammonium fluoride, often used as a catalyst, was studied. Resulting materials were characterised by XRD, SEM, N2 sorption, HR-TEM, hyperpolarised Xe NMR, pyridine sorption as well as by their stability toward boiling water. It was shown that the hydrothermal synthesis has to be carried out at 140 °C in order to better preserve the structure of the mesoporous precursor. Composite materials could be obtained only from a fluoride-free synthesis at short crystallisation times, t < 5 h. Appearance of 2-5 nm nanoparticles in some of the corresponding samples, has been related to the increase in the total acidity. Inclusion of zeolitic material in the remaining Al-SBA-15 structure was demonstrated by hyperpolarised xenon NMR studies.
Not file

Dates and versions

hal-00912818 , version 1 (02-12-2013)

Identifiers

Cite

Sami Habib, Franck Launay, Henri El Zakhem, Matjaž Mazaj, Flavien Guenneau, et al.. ZSM-5/SBA-15 microporous/mesoporous composites prepared by a microwave-assisted zeolitisation of Al-SBA-15 mesoporous solids. Materials Research Bulletin, 2013, 48, pp.1288-1295. ⟨10.1016/j.materresbull.2012.12.030⟩. ⟨hal-00912818⟩
162 View
0 Download

Altmetric

Share

Gmail Facebook Twitter LinkedIn More